RESIONE C01 Dental Castable Resin
The Product Description
C01 is a transparent green castable resin for dentistry. It is mainly used for direct investment casting of nickel-chromium and cobalt-chromium casting alloys. It is suitable for printing partial dentures, buckles, and crowns. This resin is added with plastic material and does not contain wax. It provides high hardness, sharp details and extremely high precision for the printed parts. The exquisite partial frame with thin features and some casting flexibility can also be successfully printed and cast.
Material Properties Data
| ****
METHOD
| ****
C01-DATA
---|---|---
Shore Hardness
| ****
ASTM:D2240-05
| ****
78D
Tensile Strength
| ****
ASTM: D638-14
| ****
26MPa
Flexural Strength
| ****
ASTM: D790-10
| ****
39MPa
Flexural Modulus
| ****
ASTM: D790-10
| ****
400MPa
Notched IZOD
| ****
ASTM:D256-10
| ****
6J/m
Elongation at Break
| ****
ASTM: D638-14
| ****
4.50%
Viscosity （ 25 ℃）
| ****
ASTM:D4212-10
| ****
100mpa.s
Printing
Use the standard resin settings of the printer brand you successfully printed as the “Standard Settings” (25-30°C), otherwise, use the default standard resin settings of the printer (or slicer) as the “Standard Settings”. Then follow the following method to set the settings of RESIONE resin according to the “Standard Settings”.
| Standard Settings | C01 Settings | |
|---|---|---|
| Layer Height(mm) | 50 | 50 |
| Bottom Exposure Time(s) | A | 2*A |
| Exposure Time(s) | B | 1.5*B |
| Light-off Delay (s) | D | D |
| Bottom Lift Distance(mm) | E | E |
| Lifting Distance(mm) | F | F |
| --- | --- | --- |
Bottom Lift Speed
(mm/min)
| G| G
Lifting Speed (mm/min)| H| H
Retract Speed (mm/min)| I| I
Note:
When the room temperature during printing is lower than 24℃: Every 5℃
decrease, the bottom layer and normal exposure time increase by 15%
The calculation of the above printing parameters is based on the experimental
results of the RESIONE laboratory and is for reference only
Cleaning and Post-curing
Cleaning: Use ultrasonic or 3D printing special cleaning machine with the ethanol(concentration ≥95%), or IPA to clean for less than 1 min. Please use compressed air to dry the prints after cleaning it.
No need for post-curing.
Casting Guide
STEP 1: CAD Design
STEP 2: 3D Print
STEP 3: Cleaning and post-treatment
STEP 4: Seed wax casting channel
Investment
Please follow the instructions provided by the dental investment material supplier. If you do not have dental investment material, you can refer to our scheme The most suitable temperature for preparing denta investment materials is above 20°C
- Powder : Mixed liquid
- 100g: 22ml
(Mixed liquid=Tap water 13.2ml: Dental casting liquid 6.6ml)
Note: when the temperature is lower than 1 o•c, the liquid should be adjusted to 20ml; when the temperature is lower than 5°C, the liquid should be adjusted to 18ml. If the thin edge model is not completely cast, the liquid can be appropriately reduced,
- Effective operation time: about 3-5 minutes (15-25°C), the higher the room temperature, the shorter the operation time
- Clean and wipe the mixing container before operation.
- Add the liquid first and then the powder. Mix manually for about 20 seconds and then vacuum blender for 45 seconds.Investment
- The casting ring oscillates on the oscillating machine at the lowest vibration level for 1 O seconds. The embedding of paste is carefully poured into the casting dental model, and no vibration is allowed after complete filling.
- The casting ring is removed as soon as possible after curing and heating up to about 43°C, so that the expansion is more uniform and the ring is not easy to crack
- The mould is soaked in water and let stand for 25-30 minutes to make the embedding material completely solidified
The embedded material deformation caused by moving the die or removing the casting ring prematurely may lead to micro cracks in the model
Burnout Process
Preheat the furnace to 600°C,put in furnace at 600°C, insulati on for 30 minutes is the best, adjust the heating rate of 7°C/m in to rise to 900°C, insulation for 30 minutes to 60 minutes can be cast successfully. Burnout Schedule
Note: The casting mold tilts to leave an air inlet at the bottom.The insulation time shall be adjusted according to the actual number and size of casting molds.
The alloy is fused and centrifugal filling
Take the model out and polish it