RESIONE HT100 Heat Resistant Resin Instructions
- June 9, 2024
- RESIONE
Table of Contents
HT100 Heat-resistant Resin Instruction
The Product Description
HT100 is a heat-resistant resin with a heat distortion temperature of 98°C. The prints have extremely high hardness, bending strength and tensile strength. It is resistant to long-term boiling and chemical resistance. It is used for pressing silicone rubber molds or making injection molds.
Material Properties Data
| METHOD| DATA
---|---|---
Viscosity (26G)| ASTM:D4212-10| 560mpa.s
Shore Hardness| ASTM:D2240-05| 90D
Flexural Strength| ASTM: D790-10| 108MPa
Flexural Modulus| ASTM: D790-10| 2880MPa
Tensile Strength| ASTM:D638-14| 78MPa
Elongation at Break| ASTM: 0638-14| 2.%
Notched IZOD| ASTM:D256-10| 8J/m
HDT(0.455Mpa)| ASTM:D648-18| 98t
Printing
Printing Settings: Use the standard resin settings of the printer brand you successfully printed as the “Standard Settings” (25-30°C), otherwise, use the default standard resin settings of the printer (or slicer) as the “Standard Settings”. Then follow the following method to set the settings of RESIONE resin according to the “Standard Settings”.
| Standard Settings| HT100 Settings
---|---|---
Layer Height(nun)| 50| 50
Bottom Exposure Time(s)| A| 1.25″A
Exposure Time(s)| 13| 1.
Light-off Delay (s)| I)| 134-I
Bottom Lift Distance(mm)| E| E-1-1
Lifting Distance(mm)| F| F+1
Bottom Lift Speed (mm/min)| G| G
Lifting Speed (mm/min)| H| I I
Retract Speed (mm/min)| I| I
Note:
a. When the room temperature during printing is 18℃-24℃, change the settings
as follows:
Bottom exposure time: (HT100 settings) +15%
Normal exposure time: (HT100 settings) +15%
Light-off Delay time: (HT100 settings) +1s
It is recommended to heat the resin if the printing is still not
successful.(The heating temperature is 60-80℃, heating time is 10mins). And it
is not recommended for printing at room temperature lower than 18℃
b. The lifting of some printers can be divided into two stages. All the above
settings for lifting only for to the first stage. The lifting speed of the
first stage is generally very slow, no need to change
*The calculation of the above printing parameters is based on the experimental results of the
RESIONE laboratory and is for reference only
Cleaning and Post-curing
Cleaning: You can use ultrasonic or 3D printing special cleaning machine with
the ethanol(concentration≥95%), or IPA to clean for less than 1min. Please use
compressed air to dry the prints after cleaning it.
Post-curing: If you use a post-curing box with a power of 40W, our recommended
post-curing time is about 60mins (Adjust the post-curing time according to the
power of the post-curing box, the greater the power, the shorter the time).
If there is a higher temperature resistance requirement, you can put the
prints in boiling water for 10 minutes to make it solidify more fully.
Application Guide
a. Silicone Rubber Molds(As shown below)
b. Used as an injection mold for the following thermoplastics
| Injection material | Mold temperature（℃） |
|---|---|
| PP | 10~60 |
| PS | Oct-80 |
| ABS | 50~80 |
| PMMA | 40-90 |
| PC | 80-120 |
| PA66 | 40-120 |
c. Other Application
- Test in outdoor conditions or high temperature gas/liquid environment
- Carbon fiber mold
- Metallized surface treatment such as electroplating
- Automotive interior
- Heat-resistant parts of electrical or power equipment
- Fixture For more questions, please contact [email protected]