TEST REPORT

No. : GZIN2312004129PL05_EN
Date : 2024-01-03

Scan to see the report

GZIN2312004129PL05
Verification:
check.sgsonline.com.cn

CUSTOMER NAME:  SHENZHENBAOANQUYIDEDANGKANGDIANZISHANGWUSHANGHANG
ADDRESS:                   26DONG BDONG 429, XIXIANGJIEDAO YANTIANSHEQU
YINTIANGONGYEQU, BAOAN, SHENZHEN, GUANGDONG,518100,
CHINA

Sample Name               : Newentor Mattress Topper
Manufacturer                : Newentor
Model No.                    : MT5

Above information and sample(s) was/were submitted and confirmed by the client. SGS, however, assumes no responsibility to verify the accuracy, adequacy and completeness of the sample information provided by client.


Date of Receipt           : 2023-12-06
Testing Period             : 2023-12-06 ~ 2024-01-03
Test result(s)                : For further details, please refer to the following page(s)
(Unless otherwise stated the results shown in this test report refer only to the sample(s) tested)

Signed for
SGS-CSTC Standards Technical
Services Co., Ltd. Guangzhou
Branch.


Quincey Lee
Authorized signatory

Test Result Summary

No.

| Test(s) Requested| Result(s)| Comments
---|---|---|---

1

| Low hazard in BS 7177:2008+A1:2011 Specification for resistance to ignition of mattresses, mattress pads, divans and bed bases|

PASS

| Clause 5 and 6 weren’t checked.
For further details, please refer to the following page(s)

Test Conducted:

These tests are conducted in low hazard of BS 7177:2008+A1:2011 according to the application, the test methods are based on BS EN 597-1 & 2:1995 and BS 5852-part 2:1982.

I Sample Description: Mattress

II Precondition and Test Condition

|

Temperature

| Relative Humidity| Duration
---|---|---|---

Precondition

| (23±2)°C| (50±5)%| 24h
Test Condition| 21.8°C| 50%| —

III Test Results

Clause

| Principle / Requirement|

Result

---|---|---
4| Performance requirements for resistance to ignition
4.1 Ignitability      Low hazard
4.1.1| The composite shall meet the levels of ignition resistance low hazard composite test. Both surfaces of the mattress or mattress pad shall be tested, unless they are identical.
Smouldering cigarette as specified in BS EN 597-1:1995.
Match flame equivalent as specified in BS EN 597-2:1995.|

a) PASS
b) PASS
(See Annex I)

4.1.2| All filling materials, including those used in mattress pads, shall pass the relevant test:
Polyurethane foam in block or cushion form shall pass the relevant test contained in the Annex A.|

PASS(See Annex II)

4.2| Durability of treatment
All outer covers and inner covers intended for high or very high hazard categories that have been chemically treated to reduce – their ignitability shall be subjected to the water soaking and drying procedure specified in BS 5852:2006, Annex E prior to being conditioned.|

N/A

5| Sampling and frequency of testing
A sample of each mattress, mattress pad, divan or bed base specification (ignoring differing spring types) shall be tested at the frequency specified in Table 3.
Retesting shall be carried out where there is any major basic alteration to a specification.| N/P
6| Labeling And Identification
Each mattress, upholstered mattress pad, divan or bed base shall carry a permanently attached and clearly readable label (see Figures 1 to 4). The size of the graphic part of the label shall be not less than 50 mm × 50 mm. The base colour of the label shall be white with a blue border. The word “RESISTANT” shall appear on the border and shall be white and of minimum height 5 mm. A smouldering cigarette symbol, flame symbol and the ignition source number(s) shall appear in the central white area and shall be black. Information defining additional tests shall be included on the label for very high hazard mattresses and upholstered mattress pads.
The following wording shall appear on the label:
“Conforms to BS 7177:2008 for domestic use (low hazard)” shall appear on the label.| N/P

Remark: N/A=Not Applicable, N/C=Not Conduct as per client’s request, N/P=Not Provided.

Annex I: Details of Composite test

Test Results:

The following test results relate only to the ignitability of the sample or combination of materials under the particular condition of test. They are not intended as a means of assessing the full potential fire hazard of the materials or products in use.
(A) BS EN 597-1:1995 Furniture – Assessment of the ignitability of mattresses and upholstered bed bases Part 1: Ignition source smouldering cigarette

Test Criteria

| Results
---|---
1 st|

2 nd

(A) Progressive Smouldering Ignition
(1) Any test assembly that displays escalating smouldering combustion behaviour so that it is unsafe to continue the test and active extinction is necessary;|

NO

|

NO

(2) Any test assembly that smoulders until it is largely consumed within the test duration;|

NO

|

NO

(3) Any test assembly that smoulders to its full thickness, within the duration of the test;|

NO

|

NO

(4) Any test assembly that smoulders for more than one hour;|

NO

|

NO

(5) On final examination, show evidence of charring more than 50mm in any horizontal direction from the nearest point of the original position of the source.|

NO

|

NO

(B)Flaming ignition
A flaming ignition is considered to be the occurrence of any flames initiated by a progressive smouldering source|

NO

|

NO

(C) Final examination
Immediately after completion of the test programme on the assembly, dismantle it and examine it internally for progressive smouldering ignition, if this is found, extinguish the test assembly, and record an ignition and complete the test report.|

No Ignition

Test details:

Test

| Ignition Position| After Placement of the Cigarette| Extent of Damage(mm)| Comments and Observations
---|---|---|---|---
Progressive Smouldering Time| Flame Ceased Time| Smoking Ceased Time| Width| Length|

Corner

1st

| Flat Portion| 0s| 0s| 19min36s| 5| 6| 3| #2
Tape Edge| 0s| 0s| 19min05s| 5| 7| 3| #2
2nd| Flat Portion| 0s| 0s| 18min51s| 5| 5| 3| #2
Tape Edge| 0s| 0s| 18min29s| 5| 5| 3| #2

Sub – Conclusion: PASS

(B) BS EN 597-2:1995 Furniture – Assessment of the ignitability of mattresses and upholstered bed bases
Part 2, Ignition source: match flame equivalent (15±1s).

Test Criteria

| Test Results
---|---
1 st|

2 nd

(A) Progressive Smouldering Ignition
(1) Any test assembly that displays escalating smouldering combustion behaviour so that it is unsafe to continue the test and active extinction is necessary;| NO| NO
(2) Any test assembly that smoulders until it is largely consumed within the test duration;| NO| NO
(3) Any test assembly that smoulders to its full thickness, within the duration of the test;| NO| NO
(4) Any test assembly that smoulders for more than one hour;| NO| NO
(5) On final examination, show evidence of charring more than 50mm in any horizontal direction from the nearest point of the original position of the source.| NO| NO
(B)Flaming ignition
(1) Any test specimen that escalating combustion behaviour is observed so it is unsafe to continue the test| NO| NO
(2) Any test specimen that burns until it is essentially consumed within the test duration.| NO| NO
(3) Any test specimen on which any flame front reaches its extremities or passes through its full thickness within the duration of the test.| NO| NO
(4) Any test specimen that flaming continues to more than 120s after removal of the burner.| NO| NO
(C) Final examination
Immediately after completion of the test programme on the assembly, dismantle it and examine it internally for progressive smouldering ignition, if this is found, extinguish the test assembly, and record an ignition and complete the test report.| No Ignition

Test details:

Test

| Ignition Position| Time to Extinction after Removal of the Burner(second)| Extent of Damage(mm)| Comments and Observations
---|---|---|---|---
Flame Ceased time| Smoking Ceased Time| Width| Length|

Corner

1st

| Flat Portion| 0| 6| 17| 18| 2| #3
Tape Edge| 0| 6| 15| 18| 2| #3
2nd| Flat Portion| 0| 6| 17| 20| 2| #3
Tape Edge| 0| 8| 16| 20| 2| #3

Sub – Conclusion: PASS

Annex II: Filling material test as per BS 5852

Part 2: 1982 This test, specified in Annex A of BS 7177:2008+A1:2011, is based on BS 5852 part 2:1982 using ignition source 5.
To assess the ignitability of polyurethane foam in slab or cushion form used in upholstered components when subjected to ignition 5.

Sample Details:

Filling No.

| Materials| Density
---|---|---
1| Foam|

Approximately 38.7 kg/m³

2

| Foam| Approximately 33.7 kg/m³
Specified Thickness of Specimen| (75±2) mm| Actual Thickness of Specimen|

Filling 1&2: 75mm

Precondition

| Indoor Ambient Condition|

72 h

---|---|---

Conditioning of Test Specimen and Ignition Source(s)

| Temperature: (23±2)°C; Relative Humidity: (50±5)% Duration:24 h;
Testing Enclosure (fume cupboard / room)| 24.6°C| RH 56%|

Test Results:

Filling 1:

Test Criteria

| Results
---|---
1 st **test**|

2 nd test

(A) Progressive smouldering (Clause 4.1 of BS 5852 part 2:1982)
(1) Whether progressive smouldering is observed when beyond 60 minutes after ignition of the crib|

NO

|

NO

(2) Whether escalating combustion behaviour is observed so that it is unsafe to continue the test |

NO

|

NO

(3) Whether any composite smoulders until it is essentially consumed within the test duration.|

NO

|

NO

(4) Whether any composite that smoulders to the extremities the specimen viz. upper or lower margins, either side or to its full thickness within the duration of the test|

NO

|

NO

(5) Whether any composite on final examination shows evidence of charring more than 100mm in any direction|

NO

|

NO

(B) Flaming (Clause 4.2 of BS 5852 part 2:1982)
(1) Whether any composite that continues to flame for more than 10 minutes after the ignition of the crib|

NO

|

NO

(2) Whether escalating combustion behaviour is observed so that it is unsafe to continue the test|

NO

|

NO

(3) Whether any composite is essentially consumed within the test duration|

NO

|

NO

(4) Whether any composite display that on which flame front reaches the lower margin, either side or passes through the full thickness of the specimen within the duration of the test|

NO

|

NO

(C) Mass Loss (Clause 5 in Schedule 1 Part1 of UK Regulations)
If failure against the criteria of clause 4 of BS 5852 : part 2 has occurred but only by way of damage exceeding the limits defined in A (4), (5) and B (4) above and provided that the resultant mass loss is less than 60g the foam passes the ignitability test.|

31 g

|

33 g

Test Details:

Test No.

| 1st|

2nd

---|---|---
Duration of| Ignition source (min, sec)|

02min42s

|

02min44s

Flames (min, sec)|

03min18s

|

03min40s

Smoke (min, sec)|

08min54s

|

09min28s

Extent of damage of horizontal component| Foam – Width (mm)|

92

|

96

Foam – Length (mm)|

150

|

154

Foam – Depth (mm)|

60

|

61

Extent of damage of vertical component| Foam – Length (mm)|

179

|

182

Foam – Depth (mm)|

48

|

50

The initial mass of the sample composite (g)|

7810

|

7815

The final mass of sample composite(g)|

7779

|

7782

The final mass loss of the composite(g)|

31

|

33

Rating, comments & observations|

7

|

7

Sub – Conclusion: PASS

Filling 2:

Test Criteria

| Results
---|---
1 st **test**|

2 nd test

(A) Progressive smouldering (Clause 4.1 of BS 5852 part 2:1982)
(1) Whether progressive smouldering is observed when beyond 60 minutes after ignition of the crib|

NO

|

NO

(2) Whether escalating combustion behaviour is observed so that it is unsafe to continue the test |

NO

|

NO

(3) Whether any composite smoulders until it is essentially consumed within the test duration.|

NO

|

NO

(4) Whether any composite that smoulders to the extremities the specimen viz. upper or lower margins, either side or to its full thickness within the duration of the test|

NO

|

NO

(5) Whether any composite on final examination shows evidence of charring more than 100mm in any direction|

NO

|

NO

(B) Flaming (Clause 4.2 of BS 5852 part 2:1982)
(1) Whether any composite that continues to flame for more than 10 minutes after the ignition of the crib|

NO

|

NO

(2) Whether escalating combustion behaviour is observed so that it is unsafe to continue the test|

NO

|

NO

(3) Whether any composite is essentially consumed within the test duration|

NO

|

NO

(4) Whether any composite display that on which flame front reaches the lower margin, either side or passes through the full thickness of the specimen within the duration of the test|

NO

|

NO

(C) Mass Loss (Clause 5 in Schedule 1 Part1 of UK Regulations)
If failure against the criteria of clause 4 of BS 5852 : part 2 has occurred but only by way of damage exceeding the limits defined in A (4), (5) and B (4) above and provided that the resultant mass loss is less than 60g the foam passes the ignitability test.|

32 g

|

35 g

Test Details:

Test No.

| 1st|

2nd

---|---|---
Duration of| Ignition source (min, sec)|

02min44s

|

02min45s

Flames (min, sec)|

04min25s

|

04min41s

Smoke (min, sec)|

09min30s

|

09min55s

Extent of damage of horizontal component| Foam – Width (mm)| 101| 104
Foam – Length (mm)| 152| 159
Foam – Depth (mm)| 62| 64
Extent of damage of vertical component| Foam – Length (mm)| 155| 158
Foam – Depth (mm)| 54| 57
The initial mass of the sample composite (g)| 7699| 7691
The final mass of sample composite(g)| 7667| 7656
The final mass loss of the composite(g)| 32| 35
Rating, comments & observations|

7

|

7

Sub – Conclusion: PASS

Remark: N/A— Not Applicable, N/C ­Not Conduct

1­­-Cigarette fails to smoulder its complete length;

2-­­Cigarette passes to smoulder its complete length, but the sample was not

ignition;

3-­­The sample was not ignited after removal of the burner;

4­­-Flaming but self-extinguishment;

5-­­Extinguished by operator, escalating flaming combustion;

6-­­The first test failed, so retest was not conducted.

7-Pass, flaming but self-extinguishment, the resultant mass loss is less than

60g;

8-Fail, flaming but self-extinguishment, the resultant mass loss is more than

60g;

  1. Filling 1 of this test report is extracted from the test report number SDFS2312007898FF. The Sample Receiving Date was Dec.11, 2023, The Performing Date was Dec.11, 2023 to Dec.15, 2023.
  2. Filling 2 of this test report is extracted from the test report number SDFS2312007899FF. The Sample Receiving Date was Dec.11, 2023, The Performing Date was Dec.11, 2023 to Dec.15, 2023.

Note: This document cannot be reproduced except full, without prior written approval of the Company.

Photo Appendix:

SGS MT5 Newentor Mattress Topper - a1  SGS MT5
Newentor Mattress Topper - a2

Mattress                                 Filling 1

SGS MT5 Newentor Mattress Topper - a3

Filling 2

Appendix information: The above test was carried out by Shunde Branch SGS-CSTC Co., Ltd. laboratory.

In the territory of the People’s Republic of China, the test report with CMA logo expresses that the test items are within the scope of China Metrology Accreditation(CMA); without CMA logo expresses that part/all of the test items are not within the scope of China Metrology Accreditation(CMA), and just for client internal reference.

****End of report****

Unless otherwise agreed in writing, this document is issued by the Company subject to its General Conditions of Service printed overleaf, available on request or accessible at https://www.sgs.com/en/Terms-and- Conditions, Attention is drawn to the limitation of liability, indemnification and jurisdiction issues defined therein. Any holder of this document is advised that information contained hereon reflects the Company’s findings at the time of its intervention only and within the limits of Client’s instructions, if any. The Company’ s sole responsibility is to its Client and this document does not exonerate parties to a transaction from exercising all their rights and obligations under the transaction documents. This document cannot be reproduced except in full, without prior written approval of the Company. Any unauthorized alteration, forgery or falsification of the content or appearance of this document is unlawful and offenders may be prosecuted to the fullest extent of the law. Unless otherwise stated the results shown in this test report refer only to the sample(s) tested and such sample(s) are retained for 30 days only.
Attention: To check the authenticity of testing/inspection report & certificate. please contact us at telephone: (86-755)8307 1443, or email: CN.Doccheck@sgs.com
No.198, Kezhu Road, Science City, Economic & Technological Development Area, Guangzhou, Guangdong, China 510663      t (86-20) 82155661 www.sgsgroup.com.cn
sgs.china@sgs.com


Member of the SGS Group (SGS SA)

Documents / Resources

| SGS MT5 Newentor Mattress Topper [pdf] User Manual
MT5 Newentor Mattress Topper, MT5, Newentor Mattress Topper, Mattress Topper, Topper
---|---

Read User Manual Online (PDF format)

Read User Manual Online (PDF format)  >>

Download This Manual (PDF format)

Download this manual  >>

Related Manuals