Filaments Recycled Polyamide 6 Filled With Recycled Carbon Fibers Instructions
- June 13, 2024
- Filaments
Table of Contents
Filaments Recycled Polyamide 6 Filled With Recycled Carbon Fibers
SPECIFICATION
- Printing temperature: 250–270 °C
- Heated bed temperature: 80–110 °C
- Speed: 30–50 mm/s
- Part cooling fan: 0 %
- Heated bed surface: LockPAd, mirror/glass, (PEI)
- Adhesive: Magigoo PA, PVA glue
- Raft/skirt/brim: Brim > 10mm, raft
Heated chamber/enclosure: recommended
- Preparation – Recommended to dry the filament at 80°C overnight. Temperatures below 70°C are not effective for drying.
- In-print filament delivery – We recommend delivery of the filament from a heated caddy or desiccator at 50°C to extend the printable life and increase print reliability
- Adhesion – it is recommended to use a large brim around the printed object. The best results were achieved with LockPAd and Garolite. Glass bed with PVA glue or Magigoo PA works fine.
- Although Nylons usually don’t stick well to PEI, small rounded parts are possible to print on PEI.
- Cooling – It’s necessary to turn off the part cooling fan. Too high part cooling fan speed or too fast cooling of the printed object can lead to warping and shrinking.
Storing – Airtight bag with desiccant
- In case of moist material, re-dry it in the appropriate device. The conditions to achieve optimal level of moisture are 80 °C for 5+ hours.
- Processing of moist filament may cause degradation of polymer chains, brittleness, poor layer adhesion, stringing, oozing, etc.
- Printed parts – If it’s possible at construction, avoid sharp corners touching the build plate. It can
- increase the warping effect when printing nylon.
- Nozzle – Minimum size 0.6mm, strongly recommend the use of hardened or wear-resistant nozzles
Producer: Fillamentum Manufacturing Czech s.r.o. tel.: (+420) 702 236 177